Mmepe nke batrị lithium

10 Ọkt, 2021

By hoppt

Isi mmalite nke ngwaọrụ batrị nwere ike ịmalite site na nchọpụta nke karama Leiden. Ọ bụ ọkà mmụta sayensị Dutch bụ́ Pieter van Musschenbroek bụ nke mbụ chepụtara karama Leiden na 1745. ite Leyden bụ ihe eji eme ihe mgbe ochie. Ọ na-eji mpempe akwụkwọ ọla abụọ kewapụrụ site na insulator. A na-eji mkpanaka igwe dị n'elu chekwaa ma hapụ ụgwọ. Mgbe ị na-emetụ mkpanaka ahụ Mgbe a na-eji bọọlụ ígwè, karama Leiden nwere ike idobe ma ọ bụ wepụ ike eletrik dị n'ime, ụkpụrụ na nkwadebe ya dị mfe. Onye ọ bụla nwere mmasị nwere ike ime ya n'onwe ya n'ụlọ, ma ihe ngosi nke onwe ya dị njọ karị n'ihi nduzi ya dị mfe. N'ozuzu, a ga-ewepụ ọkụ eletrik niile n'ime awa ole na ole ruo ụbọchị ole na ole. Agbanyeghị, mpụta karama Leiden gosipụtara ọkwa ọhụrụ na nyocha nke ọkụ eletrik.

Kalama Leiden

N'afọ ndị 1790, ọkà mmụta sayensị Ịtali bụ Luigi Galvani chọpụtara iji zinc na ọla kọpa wires jikọọ ụkwụ frog wee chọpụta na ụkwụ frog ga-atụgharị, ya mere ọ tụrụ aro echiche nke "bioelectricity." Nchọpụta a mere ka ọkà mmụta sayensị Italy bụ Alessandro kụda mmụọ. Nkwenye Volta, Volta kwenyere na ntugharị nke ụkwụ frog na-abịa site na ọkụ eletrik nke igwe na-emepụta karịa ọkụ eletrik dị na frog. Iji gbaghaa echiche Galvani, Volta tụrụ aro Volta Stack ya ama ama. Nchịkọta voltaịk ahụ nwere mpempe zinc na ọla kọpa nwere kaadiboodu etinyere na mmiri nnu n'etiti. Nke a bụ ihe atụ nke batrị kemịkal a tụrụ aro.
Usoro mmeghachi omume electrode nke cell voltaic:

nti electrode: 2H^++2e^-→H_2

electrode ọjọọ: Zn→〖Zn〗^(2+)+2e^-

Voltaic tojupụtara

Na 1836, ọkà mmụta sayensị Britain bụ John Frederic Daniell chepụtara batrị Daniel iji dozie nsogbu nke ikuku ikuku na batrị. Batrị Daniel nwere ụdị mbụ nke batrị kemịkalụ ọgbara ọhụrụ. Ọ nwere akụkụ abụọ. Akụkụ dị mma na-emikpu na ngwọta sulfate ọla kọpa. Akụkụ nke ọzọ nke ọla kọpa bụ zinc na-emikpu na ngwọta zinc sulfate. Batrị Daniel mbụ ahụ jupụtara na ngwọta sulfate ọla kọpa n'ime ite ọla kọpa ma tinye akpa seramiiki porous cylindrical n'etiti. N'ime akpa seramiiki a, enwere mkpanaka zinc na zinc sulfate dị ka electrode na-adịghị mma. Na ngwọta, obere oghere dị n'ime akpa seramiiki na-ekwe ka igodo abụọ gbanwee ions. Batrị Daniel nke oge a na-ejikarị àkwà mmiri nnu ma ọ bụ membranes nke nwere ike ime ka ọ nweta mmetụta a. Ejiri batrị Daniel mee ihe dị ka isi iyi ike maka netwọk telegraph ruo mgbe batrị akọrọ dochie ha.

Usoro mmeghachi omume electrode nke batrị Daniel:

Eletrọd dị mma: 〖Cu〗^(2+)+2e^-→Cu

electrode ọjọọ: Zn→〖Zn〗^(2+)+2e^-

Daniel batrị

Ka ọ dị ugbu a, a chọpụtala ụdị isi nke batrị ahụ, nke gụnyere electrode dị mma, electrode na-adịghị mma, na electrolyte. Na ndabere dị otú ahụ, batrị enweela ọganihu ngwa ngwa n'ime 100 afọ na-esote. Ọtụtụ usoro batrị ọhụrụ apụtala, gụnyere ọkà mmụta sayensị France bụ Gaston Planté chepụtara batrị lead-acid na 1856. Batrị Lead-acid nnukwu mmepụta ya ugbu a na ọnụ ala dị ala adọtala mmasị sara mbara, n'ihi ya, a na-eji ya n'ọtụtụ ngwaọrụ mkpanaka, dị ka ọkụ eletrik mbụ. ugbo ala. A na-ejikarị ya dị ka nkwado ndabere na mpaghara maka ụfọdụ ụlọ ọgwụ na ọdụ ọdụ. Batrị lead-acid na-abụkarị nke lead, lead dioxide, na sulfuric acid ngwọta, voltaji ha nwere ike iru ihe dịka 2V. Ọbụlagodi n'oge a, ebipụbeghị batrị lead-acid n'ihi teknụzụ ha tozuru oke, ọnụ ahịa dị ala, yana sistemu mmiri dị mma.

Usoro mmeghachi omume electrode nke batrị lead-acid:

Positive electrode: PbO_2+〖SO〗_4^(2-)+4H^++2e^-→Pb〖SO〗_4+2H_2 O

Eletrọd na-adịghị mma: Pb+〖SO〗_4^(2-)→Pb〖SO〗_4+2e^-

Batrị Lead-acid

Batrị nickel-cadmium, nke onye ọkà mmụta sayensị Sweden bụ Waldemar Jungner chepụtara na 1899, bụ nke a na-ejikarị eme ihe na obere ngwaọrụ eletrọnịkị mkpanaaka, dị ka ndị na-eje ije n'oge, n'ihi njupụta ume ya dị elu karịa batrị lead-acid. Yiri batrị lead-acid. A na-ejikwa batrị nickel-cadmium eme ihe kemgbe 1990s, mana nsi ha dị oke elu, batrị n'onwe ya nwekwara mmetụta ebe nchekwa kpọmkwem. Nke a bụ ya mere anyị ji anụkarị ụfọdụ ndị toro eto na-ekwu na a ga-agbachasịsịa batrị ahụ tupu ya etinyere ya na batrị mkpofu ga-emerụ ala, na ihe ndị ọzọ. (Rịba ama na ọbụna batrị ndị dị ugbu a na-egbu egbu nke ukwuu na e kwesịghị ịtụfu ya n'ebe niile, ma batrị lithium dị ugbu a enweghị uru ebe nchekwa, na nfefe karịrị akarị na-emerụ ndụ batrị.) Batrị Nickel-cadmium na-emebi gburugburu ebe obibi, na ha. Nguzogide dị n'ime ga-agbanwe na okpomọkụ, nke nwere ike imebi n'ihi oke oke ugbu a n'oge ịchaji. Batrị nickel-hydrogen ji nwayọọ nwayọọ kpochapụ ya n'ihe dị ka afọ 2005. Ka ọ dị ugbu a, a naghị ahụ batrị nickel-cadmium n'ahịa.

Ngụkọ mmeghachi omume electrode nke batrị nickel-cadmium:

Positive electrode: 2NiO(OH)+2H_2 O+2e^-→2OH^-+2Ni〖(OH)〗_2

Eletrọd na-adịghị mma: Cd+2OH^-→Cd〖(OH)〗_2+2e^-

Batrị nickel-cadmium

Lithium metal batrị ogbo

N'afọ ndị 1960, ndị mmadụ mechara banye n'ọchịchị nke oge batrị lithium.

Achọpụtara metal lithium n'onwe ya na 1817, n'oge na-adịghịkwa anya ndị mmadụ chọpụtara na a na-eji ihe anụ ahụ na kemịkal lithium metal eme ihe dị ka ihe maka batrị. Ọ nwere obere njupụta (0.534g 〖cm〗^(-3)), nnukwu ikike (usoro iwu ruo 3860mAh g^(-1)), na ikike ya dị ala (-3.04V ma e jiri ya tụnyere ọkọlọtọ hydrogen electrode). Ndị a na-fọrọ nke nta ịgwa ndị mmadụ na m na-adịghị mma electrode ihe nke ezigbo batrị. Otú ọ dị, lithium metal n'onwe ya nwere nnukwu nsogbu. Ọ na-arụsi ọrụ ike, na-eji mmiri eme ihe ike, ma nwee nnukwu ihe achọrọ na gburugburu ebe ọrụ. Ya mere, ruo ogologo oge, ndị mmadụ enweghị enyemaka na ya.

Na 1913, Lewis na Keyes tụlere ikike nke electrode metal lithium. Ma mee ule batrị na lithium iodide na ngwọta propylamine dị ka electrolyte, n'agbanyeghị na ọ dara.

N'afọ 1958, William Sidney Harris kwuru na akwụkwọ mmụta doctoral ya na o tinyere lithium metal na ngwọta ester organic dị iche iche wee hụ ka e hiwere usoro nke passivation layers (gụnyere lithium metal na perchloric acid). Lithium LiClO_4

Ihe dị na ngwọta PC nke propylene carbonate, ihe ngwọta a bụ usoro electrolyte dị mkpa na batrị lithium n'ọdịnihu), na a hụwo ihe dị iche iche nke nnyefe ion, ya mere, e mewo ụfọdụ nnwale electrodeposition mbụ dabere na nke a. Nnwale ndị a butere n'ihu ọha na mmepe nke batrị lithium.

N'afọ 1965, NASA mere nnyocha miri emi na ihe nchaji na ịchaji nke Li||Cu batrị na lithium perchlorate PC ngwọta. Usoro electrolyte ndị ọzọ, gụnyere nyocha nke LiBF_4, LiI, LiAl〖Cl〗_4, LiCl, Nchọpụta a kpalitere mmasị dị ukwuu na sistemu electrolyte organic.

N'afọ 1969, otu patent gosiri na mmadụ amalitela ịgbalị iji lithium, sodium, na potassium metals ahịa batrị.

Na 1970, Panasonic Corporation nke Japan chepụtara batrị Li‖CF_x┤, ebe oke x na-abụkarị 0.5-1. CF_x bụ fluorocarbon. Ọ bụ ezie na fluorine gas na-egbu egbu nke ukwuu, fluorocarbon n'onwe ya bụ ntụ ntụ na-adịghị ọcha na-adịghị egbu egbu. Enwere ike ikwu na mpụta batrị Li‖CF_x ┤ bụ ezigbo batrị lithium nke izizi. Li‖CF_x┤ batrị bụ batrị bụ isi. N'agbanyeghị nke ahụ, ikike ya buru ibu, ikike ikike ya bụ 865mAh ‖Kg〗^(-1), na voltaji mwepu ya kwụsiri ike na ogologo oge. N'ihi ya, ike ahụ kwụsiri ike na ihe mgbapụta onwe ya dị ntakịrị. Mana ọ nwere nnukwu arụmọrụ ọnụego ya enweghị ike ịgba ụgwọ. Ya mere, a na-ejikọta ya na manganese dioxide n'ozuzu iji mee batrị Li‖CF_x ┤-MnO_2, nke a na-eji dị ka batrị dị n'ime maka ụfọdụ obere sensọ, clocks, wdg, na-ewepụbeghị.

Eletrọd dị mma: CF_x+xe^-+x〖Li〗^+→C+xLiF

Eletrọd na-adịghị mma: Li→〖Li〗^++e^-

Li|| CFx batrị schematic

N'afọ 1975, ụlọ ọrụ Sanyo nke Japan chepụtara batrị Li‖MnO_2┤, nke e bu ụzọ jiri mee ihe na mgbako anyanwụ nwere ike ịgbanye. Enwere ike were nke a dị ka batrị lithium mbụ enwere ike chaji. Ọ bụ ezie na ngwaahịa a bụ nnukwu ihe ịga nke ọma na Japan n'oge ahụ, ndị mmadụ enweghị nghọta miri emi banyere ihe dị otú ahụ na ha amaghị lithium na manganese dioxide. Kedu ụdị ihe kpatara mmeghachi omume ahụ?

N'ihe fọrọ nke nta ka ọ bụrụ n'otu oge ahụ, ndị America nọ na-achọ batrị ọzọ, nke anyị na-akpọ ugbu a batrị nke abụọ.

Na 1972, MBArmand (aha ụfọdụ ndị ọkà mmụta sayensị na-adịghị sụgharịa na mmalite) tụrụ aro na a ogbako akwụkwọ M_(0.5) Fe 〖(CN)〗_3 (ebe M bụ alkali metal) na ihe ndị ọzọ na-acha anụnụ anụnụ Prussian Ọdịdị. , Ma mụọ ya ion intercalation onu. Na 1973, J. Broadhead na ndị ọzọ nke Bell Labs mụrụ intercalation onu nke sọlfọ na ayodiin atọm na metal dichalcogenides. Ọmụmụ ihe mmalite ndị a gbasara ihe ngbanwe nke ion bụ ihe kacha mkpa na-anya ụgbọ ala maka ọganihu nwayọọ nwayọọ nke batrị lithium. Nchọpụta izizi bụ nke ziri ezi n'ihi ọmụmụ ihe ndị a na-emesịa batrị lithium-ion ga-ekwe omume.


Na 1975, Martin B. Dines nke Exxon (onye bu ụzọ nke Exxon Mobil) mere mgbakọ mbụ na nyocha na intercalation n'etiti usoro mgbanwe metal dichalcogenides na alkali ọla na n'otu afọ, Exxon bụ aha ọzọ Scientist MS Whittingham bipụtara patent. na Li‖TiS_2┤ ọdọ mmiri. Na 1977, Exoon kwadoro batrị dabere na Li-Al‖TiS_2┤, nke lithium aluminum alloy nwere ike ime ka nchekwa batrị dịkwuo elu (ọ bụ ezie na a ka nwere nnukwu ihe ize ndụ). Mgbe nke ahụ gasịrị, Everready ejirila sistemụ batrị dị otú ahụ mee ihe n'usoro na United States. Azụmahịa nke ụlọ ọrụ batrị na ụlọ ọrụ Grace. Batrị Li‖TiS_2 ┤ nwere ike ịbụ batrị lithium nke abụọ nke mbụ n'ezie, ọ bụkwa sistemu batrị kacha ewu ewu n'oge ahụ. N'oge ahụ, njupụta ike ya dị ihe dị ka okpukpu 2-3 karịa nke batrị lead-acid.

Eserese atụmatụ nke mbido Li|| batrị TiS2

Eletrọd dị mma: TiS_2+xe^-+x〖Li〗^+→〖Li〗_x TiS_2

Eletrọd na-adịghị mma: Li→〖Li〗^++e^-

N'otu oge ahụ, onye ọkà mmụta sayensị Canada MA Py chepụtara batrị Li‖MoS_2┤ na 1983, nke nwere ike inwe njupụta ume nke 60-65Wh 〖Kg〗^(-1) na 1/3C, nke dabara na Li‖TiS_2┤ batrị. Dabere na nke a, n'afọ 1987, ụlọ ọrụ Canada Moli Energy weputara batrị lithium a na-ere ahịa n'ezie, nke a na-achọkarị n'ụwa niile. Nke a kwesịrị ịbụ ihe omume dị ịrịba ama na akụkọ ihe mere eme, mana ihe ịtụnanya bụ na ọ na-ebutekwa ọdịda Moli ma emechaa. Mgbe ahụ n'oge opupu ihe ubi nke 1989, Moli Company weputara ngwaahịa batrị Li‖MoS_2┤ ọgbọ nke abụọ ya. Na ngwụcha oge opupu ihe ubi nke 1989, ngwaahịa batrị Li‖MoS_2┤ ọgbọ mbụ Moli gbawara wee bute oke ụjọ. N'oge okpomọkụ nke otu afọ, a na-echeta ngwaahịa niile, a na-akwụkwa ndị ahụ tara ahụhụ ụgwọ. N'ọgwụgwụ nke otu afọ ahụ, Moli Energy kwupụtara na ọ dara akụ na NEC nke Japan nwetara ya n'oge opupu ihe ubi nke 1990. Ọ dị mma ikwu na a nụrụ kepu kepu na Jeff Dahn, onye Canada bụ ọkà mmụta sayensị n'oge ahụ, na-eduzi ọrụ batrị na Moli. Ike wee gbaa arụkwaghịm n'ihi mmegide ọ na-aga n'ihu na ndepụta batrị Li‖MoS_2┤.

Eletrọd dị mma: MoS_2+xe^-+x〖Li〗^+→〖Li〗_x MoS_2

Eletrọd na-adịghị mma: Li→〖Li〗^++e^-

Taiwan enwetala batrị 18650 nke Moli Energy mepụtara ugbu a

Ka ọ dị ugbu a, batrị igwe lithium ejirila nwayọọ nwayọọ pụọ n'ihu ọha. Anyị nwere ike ịhụ na n'ime oge site na 1970 ruo 1980, nchọpụta ndị ọkà mmụta sayensị mere na batrị lithium lekwasịrị anya na ngwa cathode. Ebumnuche ikpeazụ na-elekwasị anya mgbe niile na dichalcogenides metal mgbanwe. N'ihi nhazi ha dị larịị (ngbanwe metal dichalcogenides na-amụ ugbu a dị ka ihe nwere akụkụ abụọ), akwa ha na enwere oghere zuru oke n'etiti akwa akwa iji nabata ntinye nke ion lithium. N'oge ahụ, enwere ntakịrị nyocha banyere ihe anode n'ime oge a. N'agbanyeghị na ụfọdụ ọmụmụ lekwasịrị anya na alloy nke lithium metal iji welie nkwụsi ike ya, lithium metal n'onwe ya adịghị akwụsi ike ma dị ize ndụ. Ọ bụ ezie na mgbawa batrị Moli bụ ihe omume juru ụwa anya, enweela ọtụtụ ihe mgbawa nke batrị igwe lithium.

Ọzọkwa, ndị mmadụ amaghị ihe kpatara mgbawa nke batrị lithium nke ọma. Tụkwasị na nke ahụ, a na-ewere lithium metal dị ka ihe electrode na-adịghị mma nke na-adịghị edochi anya n'ihi àgwà ọma ya. Mgbe batrị Moli gbawara, nnabata ndị mmadụ na batrị lithium metal dara ada, na batrị lithium batara n'oge ọchịchịrị.

Iji nweta batrị dị nchebe karị, ndị mmadụ ga-eji ihe electrode na-emerụ ahụ malite. N'agbanyeghị nke ahụ, enwere nsogbu dị iche iche ebe a: ikike nke lithium metal na-emighị emi, na iji ihe ndị ọzọ na-emepụta ihe na-adịghị mma ga-eme ka ikike electrode na-adịghị mma dịkwuo mma, na otú a, batrị lithium batrị ga-ebelata ihe dị iche iche nwere ike ime, nke ga-ebelata. ike njupụta nke oké ifufe. Ya mere, ndị ọkà mmụta sayensị ga-achọta ihe kwekọrọ na cathode elu voltaji. N'otu oge ahụ, electrolyte batrị ga-adabarịrị na voltaji dị mma na nke na-adịghị mma na nkwụsi ike okirikiri. N'otu oge ahụ, conductivity nke electrolyte Na okpomọkụ na-eguzogide dị mma. Usoro ajụjụ a juru ndị ọkà mmụta sayensị anya ogologo oge ịhụ azịza na-eju afọ karị.

Nsogbu mbụ ndị ọkà mmụta sayensị ga-edozi bụ ịchọta ihe dị mma, ihe na-emerụ ahụ nke nwere ike dochie ígwè lithium. Lithium metal n'onwe ya nwere oke ọrụ kemịkalụ, na usoro nsogbu nke uto dendrite adịwo ike na gburugburu ebe obibi na ọnọdụ, ọ dịghịkwa mma. Graphite bụ ugbu a bụ isi nke electrode na-adịghị mma nke batrị lithium-ion, a na-amụkwa ngwa ya na batrị lithium n'oge dị ka 1976. Na 1976, Besenhard, JO emeela nyocha zuru ezu na njikọ electrochemical nke LiC_R. Otú ọ dị, n'agbanyeghị graphite nwere magburu onwe Njirimara (elu conductivity, elu ikike, ala ikike, inertness, wdg), n'oge ahụ, electrolyte eji na lithium batrị bụ n'ozuzu PC ngwọta nke LiClO_4 kwuru n'elu. Graphite nwere nnukwu nsogbu. Na enweghị nchebe, ụmụ irighiri ihe ndị na-ahụ maka PC ga-abanyekwa na nhazi graphite na njikọ lithium-ion, na-ebute mbelata arụmọrụ okirikiri. Ya mere, ndị ọkà mmụta sayensị akwadoghị graphite n'oge ahụ.

Banyere ihe cathode, mgbe nyocha nke ọkwa batrị lithium metal, ndị ọkà mmụta sayensị chọpụtara na lithium anode n'onwe ya bụkwa ihe nchekwa lithium nwere ntụgharị dị mma, dị ka LiTiS_2, 〖Li〗_x V〖Se〗_2 (x = 1,2) na ihe ndị ọzọ, na ndabere nke a, 〖Li〗_x V_2 O_5 (0.35≤x<3), LiV_2 O_8 na ihe ndị ọzọ ka emepụtara. Na ndị ọkà mmụta sayensị ejirila nke nta nke nta mara nke ọma ụdị ọwa ion dị iche iche nke 1 (1D), 2-dimensional layered ion intercalation (2D), na usoro netwọk mgbasa ozi 3-akụkụ ion.

Prọfesọ John B. Goodenough nyocha kachasị ama na LiCoO_2 (LCO) mekwara n'oge a. Na 1979, Goodenougd et al. sitere n'ike mmụọ nsọ na otu akụkọ gbasara nhazi nke NaCoO_2 na 1973 wee chọpụta LCO wee bipụta akụkọ patent. LCO nwere usoro ngbanwe dị n'ụdị dị ka igwe ngbanwe nke disulfides, nke enwere ike itinye ion lithium n'ụzọ ọzọ wee wepụta ya. Ọ bụrụ na a na-ewepụta ion lithium kpamkpam, a ga-emepụta ihe dị nso nke CoO_2, ma enwere ike tinye ya na lithium ion maka lithium (N'ezie, batrị n'ezie agaghị ekwe ka e wepụta ion lithium kpamkpam, nke na-eme ka ọ bụrụ na ọ ga-eme ka ọ bụrụ na ọ ga-eme ka ọ bụrụ na ọ ga-eme ka ọ bụrụ na ọ dị mkpa. ga-eme ka ikike ree ngwa ngwa). Na 1986, Akira Yoshino, onye ka na-arụ ọrụ na Asahi Kasei Corporation na Japan, jikọtara atọ nke LCO, coke, na LiClO_4 PC ngwọta maka oge mbụ, na-aghọ nke mbụ ọgbara ọhụrụ lithium-ion batrị na-aghọ ugbu a lithium nkume isi nkuku nke batrị. Sony chọpụtara ngwa ngwa patent LCO nke agadi "dị mma" wee nweta ikike iji ya. N'afọ 1991, ọ mebere batrị LCO lithium-ion. Echiche nke batrị lithium-ion pụtakwara n'oge a, echiche ya na-agakwa n'ihu ruo taa. (Ọ dị mma ịmara na batrị lithium-ion nke Sony nke mbụ na Akira Yoshino na-ejikwa carbon siri ike dị ka electrode na-adịghị mma kama graphite, ihe kpatara ya bụ na PC dị n'elu nwere njikọ na graphite)

Eletrọd dị mma: 6C+xe^-+x〖Li〗^+→〖Li〗_x C_6

Eletrọd na-adịghị mma: LiCoO_2→〖Li〗_(1-x) CoO_2+x〖Li〗^++xe^-

Ihe ngosi nke ọgbọ mbụ nke batrị lithium-ion nke Sony

N'aka nke ọzọ, na 1978, Armand, M. tụrụ aro iji polyethylene glycol (PEO) dị ka a siri ike polymer electrolyte dozie nsogbu n'elu na graphite anode na-adị mfe agbakwunyere na ihe mgbaze PC ụmụ irighiri ihe ( mainstream electrolyte n'oge ahụ ka na-eji PC, DEC agwakọta ngwọta), nke na-etinye graphite n'ime sistemụ batrị lithium maka oge mbụ, ma tụpụta echiche nke batrị oche oche (oche mkpatụ) n'afọ na-esote. Echiche dị otú ahụ ka na-aga n'ihu ruo ugbu a. Sistemụ electrolyte bụ isi ugbu a, dị ka ED/DEC, EC/DMC, wdg, ji ​​nwayọọ nwayọọ pụta na 1990s wee na-eji ya kemgbe ahụ.

N'otu oge ahụ, ndị ọkà mmụta sayensị nyochakwara usoro batrị: Li‖Nb〖Se〗_3 ┤ batrị, Li‖V〖SE〗_2┤ batrị, Li‖〖Ag〗_2 V_4 ┤ O_11 batrị, batrị Li․ Li ‖I_2 ┤Batteries, wdg, n'ihi na ha bara uru ugbu a, na ọ dịghị ọtụtụ ụdị nke nnyocha nke mere na agaghị m ewebata ha n'ụzọ zuru ezu.

Oge mmepe batrị lithium-ion mgbe 1991 bụ oge anyị nọ ugbu a. N'ebe a, agaghị m achịkọta usoro mmepe n'ụzọ zuru ezu ma na-ewebata usoro kemịkal nke obere batrị lithium-ion ole na ole.

Okwu mmalite maka sistemụ batrị lithium-ion dị ugbu a, ebe a bụ akụkụ na-esote.